ČSN 630002 - Gumárenská terminologie
| Stáhnout normu: | ČSN 630002 (Zobrazit podrobnosti) Zákazníci, kteří mají na svém počítači sjednanou od České agentury pro standardizaci (ČAS) službu ČSN on-line pro elektronický přístup do plných textů norem v pdf (verzi pro firmy nebo pro jednotlivce), mohou zde přímo otevírat citované ČSN. |
| Datum vydání/vložení: | 2005-11-01 |
| Třidící znak: | 630002 |
| Obor: | Pryžové výrobky, všeobecně |
| ICS: |
|
| Stav: | Platná |
- 1 UV absorber light stabilizer
- 3 dibutyl phthalate absorption number
- 5 oil absorption number (OAN)
- 7 adhesion
- 9 adiabatic extrusion autothermal extrusion
- 11 addition polymerization
- 13 agglomeration
- 15 agglomerate
- 18 aggregate
- 20 acrylic rubber (ACM, AEM)
- 22 activator
- 24 kicker
- 26 vulcanization activator
- 28 active zinc oxide
- 30 alkane
- 32 alkene olefin
- 34 alternating copolymer
- 36 strain amplitude
- 38 anaerobic adhesive
- 40 anionic polymerization
- 42 antiblocking agent
- 44 antidegradant
- 46 staining antidegradant
- 48 non-staining antidegradant
- 50 anticoagulant
- 52 antioxidant
- 54 antiozonant
- 56 antistatic agent
- 58 applied skin
- 60 size finish
- 62 aromatic oil
- 64 atactic polymer
- 66 attritor
- 68 autoclave
- 70 automatic ejection
- 72 autoheating screw self-heating screw
- 74 balata
- 76 wrapping
- 78 light fastness colour fastness (on exposure to light)
- 80 colour
- 82 colorant
- 84 dyestuff
- 86 tinting strength
- 88 whiteness
- 90 ram
- 92 rotorless curemeter
- 94 solventless adhesive solvent-free adhesive
- 96 screwless extruder
- 98 white spots wet spots virgin rubber (depreciated)
- 100 biological resistance
- 102 biological stabilizer
- 104 block
- 106 bulk polymerization mass polymerization
- 108 block copolymer
- 110 swelling
- 112 tip (of rotor)
- 114 bubble
- 116 acrylonitrile-butadiene rubber (NBR) nitrile rubber
- 118 butadiene rubber (BR)
- 120 styrene-butadiene rubber (SBR)
- 122 butyl rubber (IIR)
- 124 total sulphur
- 126 total solids (TS) residue after drying
- 128 spider line
- 130 pot life working life
- 132 particle
- 134 KOH number
- 136 plasticity number
- 138 volatile fatty acid number
- 140 strainer
- 142 straining
- 144 dose
- 146 deflocculating agent deflocculant
- 148 strain deformation
- 150 mould swelling
- 152 polymer degradation
- 154 bar mould
- 156 split screw parted screw
- 158 parting plane
- 160 chain length
- 162 deodorant deodorizer
- 164 depolymerization
- 166 derivative
- 168 embossing
- 170 platen
- 172 polymer destruction
- 174 devulcanization
- 176 hydroperoxide scavenger hydroperoxide deactivator
- 178 dielectric strength
- 180 dielectric heating
- 182 diene diolefin
- 184 diene rubber
- 186 hole pinhole
- 188 dispersion
- 190 dispersing agent
- 192 dispersion
- 194 dispersion adhesive
- 196 dispersion polymerization
- 198 molar weight distribution
- 200 pellet size distribution
- 202 molar (molecular) mass distribution curve molar (molecular) weight distribution curve
- 204 closed assembly time
- 206 moulding cycle time
- 208 moulding time
- 210 scorch time
- 212 open assembly time
- 214 mould filling time
- 216 dwell time residence time
- 218 dry tack time
- 220 afterbake stoving postheating
- 222 aftercure postcure
- 224 bottom ejection
- 226 upstroke press
- 228 sulphur donor
- 230 conveyor conveyer
- 232 granulate conveyor granulate feeder
- 234 pressure pad
- 236 flash land
- 238 holding pressure
- 240 smouldering
- 242 aftercure postcure
- 244 maturation
- 246 crushing breaking
- 248 roughness
- 250 crusher
- 252 phr
- 254 hose lining
- 256 mould cavity
- 258 hollow article
- 260 twin-screw extruder
- 262 two-roll mill roll mill open mill
- 267 dynamic vulcanization
- 269 dynamic stress
- 271 root-mean-square strain
- 273 root-mean-square stress
- 275 elasticity
- 277 elastic deformation
- 279 elastomer
- 281 electric breakdown electric disruption
- 283 electrodecantation
- 285 electromagnetic separator
- 287 emulsification
- 289 emulsifier
- 291 emulsion
- 293 emulsion polymerization
- 295 epichlorhydrin rubber (CO, ECO)
- 297 ester-urethane rubber (AU)
- 299 floating plate
- 301 multiplaten press multidaylight press
- 303 ether-urethane rubber (EU)
- 305 ethylene-propylene rubber (EPM, EPDM)
- 307 extractable sulphur
- 309 extraction stain
- 311 extrudate
- 313 factice
- 315 phase state
- 317 film
- 319 flexometer
- 321 flocculating agent flocculant
- 323 fluorocarbon rubber (FPM, FKM, FFKM, CFM)
- 325 film
- 327 mould
- 329 photooxidation
- 331 mineral rubber
- 333 physical expanding
- 335 physical modification
- 337 gel
- 339 (rubber) gel
- 341 Gough-Joule effect
- 343 granulate granular compound
- 345 granulation
- 347 granulated rubber beaded rubber
- 349 guayule rubber
- 351 rubber compound
- 353 rubber-metal
- 355 rubber-metal spring
- 357 friction calender
- 359 gutta-percha
- 361 hose
- 363 hose assembly
- 365 woven hose
- 367 braided hose
- 369 spiralled hose
- 371 knitted hose
- 373 wrapped ply hose
- 375 hard wall hose
- 377 Hevea brasiliensis
- 379 gravimetric feeding
- 381 rotor
- 383 kneading
- 385 internal mixer kneader
- 390 homogenization
- 392 compatibilizer
- 394 homopolymer
- 396 top ejection
- 398 downstroke press
- 400 burn, noun
- 402 flammability combustibility
- 404 sponge rubber
- 406 die
- 408 network chain density
- 412 hydraulic press
- 414 rubber hydrochloride
- 416 hydrolysis
- 418 hydromechanical press
- 420 hysteresis
- 422 hysteresis loop
- 424 hysteresis loss
- 426 chemical modification
- 428 chemical resistance
- 430 chemical foaming
- 432 cooling jig cooling fixture shrinkage block shrinkage jig
- 434 refrigerator
- 436 chlorinated rubber
- 438 chloroprene rubber (CR)
- 440 chlorsulfonated polyethylene (CSM)
- 442 ideal elastic deformation
- 444 die line
- 446 impregnation proofing
- 448 impregnating agent
- 450 impregnating machine impregnator
- 452 index of non-uniformity index of polydispersity degree of polydispersity
- 454 abrasion resistance index
- 456 plasticity retention index
- 458 induction heating
- 460 inert filler
- 462 inhibitor
- 464 scorch inhibitor pre-vulcanization inhibitor
- 466 intrusion flow moulding
- 468 inverse coating
- 470 ionic polymerization
- 472 isoprene rubber (IR) synthetic polyisoprene
- 474 insulation resistance
- 476 isomer
- 478 isotactic polymer
- 480 single-cavity mould
- 482 single-screw extruder
- 484 fine particles
- 486 iodine adsorption number
- 488 rosin colophony
- 490 calibration gauging sizing
- 492 channel black
- 494 liquid curing medium salt bath
- 496 liquid rubber
- 498 capillary viscometer
- 500 carboxylated rubber
- 502 rotary moulding
- 504 cationic polymerization
- 506 rubber
- 508 oil-extended rubber
- 510 rubber-like state viscoelastic state
- 512 rubber tree
- 514 rubber poison
- 516 rubber latex
- 518 rubber sol
- 520 rubber hydrocarbon
- 522 viscosity/density ratio
- 524 V-belt
- 526 talcing
- 528 wicking
- 530 coagulant dipping
- 532 coagulant
- 534 coagulate
- 536 pin core
- 538 insert pin
- 540 pin barrel extruder
- 542 colloid mill
- 544 (mixer) chamber
- 546 assembling
- 548 complex Young’s modulus
- 550 complex shear modulus
- 552 composting
- 554 composite material composite
- 558 compression ratio
- 560 crosslink concentration crosslink density
- 562 concentration coefficient of vulcanization
- 564 masterbatch mother stock
- 566 natural latex concentrate
- 568 tube ending
- 570 conditioning
- 572 environmental conditioning
- 574 building
- 576 tyre-building drum
- 578 tack
- 580 building machine
- 582 tyre building machine
- 584 configuration
- 586 conformation
- 588 contact adhesive
- 590 contact stain
- 592 continuous vulcanization
- 594 conventional vulcanizing system
- 596 preservative
- 598 preserved rubber latex stabilized rubber latex
- 600 copolymer
- 602 copolymerization
- 604 cord (fabric)
- 606 cord fabric V-belt
- 608 corrosion
- 610 stress cracking
- 612 anchor plate
- 614 crater pit hole
- 616 beading (the end)
- 618 necking
- 620 creep
- 622 creep modulus
- 624 crystalline state
- 626 chalking
- 628 ball mill
- 630 skin
- 632 breaker plate
- 634 latex
- 636 latex foam
- 638 latex compound
- 640 cellular material
- 642 core cellular material
- 644 sponge material open cell foam
- 646 foamed material
- 648 expanded rubber
- 650 cellular hard rubber cellular ebonite
- 652 expanded adhesive
- 654 expanding
- 656 structural foam
- 658 bonding
- 660 solvent bonding
- 662 adhesive
- 664 gloss
- 666 mechanical fatigue limit
- 668 limiting oxygen index
- 670 limiting threshold strain
- 672 linear polymer
- 674 press
- 676 moulding cycle
- 678 compression mould
- 680 moulding force
- 682 moulding pressure
- 684 compression moulding
- 686 direct compacting
- 688 impact moulding
- 690 bag moulding
- 692 casting
- 694 logarithmic decrement
- 696 fatigue breakdown
- 698 dipping
- 700 dipped article
- 702 macromolecule
- 704 macromolecular substance
- 706 macroradical
- 708 lubricant
- 710 mould-release agent mould lubricant
- 712 mechanical stability
- 714 mechanical conditioning
- 716 mechanical gasket
- 718 mechano-chemical modification
- 720 mechanical press
- 722 mechanical loss factor, tg (
- 724 mechanical loss angle
- 726 cellular rubber
- 728 soft rubber
- 730 specific gravity
- 732 specific heat capacity
- 734 measured length gauge length
- 736 dynamic fatigue life
- 738 yield point tensile strength at yield
- 740 flexural strength flex resistance
- 742 shear strength
- 743 maximum stress developed in the test piece, defined as τ = F / S, where F is the force acting on cross section S; under prescribed conditions the test piece breaks at this stress
- 744 International Rubber Hardness Degrees (IRHD)
- 746 leakage flow
- 748 migration
- 750 migration stain
- 752 mixer agitator
- 754 mixing
- 756 microporous rubber
- 758 microhardness
- 760 (oil treated) rubber-maker sulphur
- 762 grinding
- 764 ground vulcanized rubber
- 766 grinding mill
- 768 modification
- 770 rubber chain modification at vulcanization
- 772 polymer modification
- 774 modifier
- 776 modulus of elasticity complex modulus of elasticity
- 778 Young’s modulus
- 780 shear modulus
- 782 molar weight molar mass
- 784 molecular mass molecular weight
- 786 monomer
- 788 monomeric unit mer
- 790 mottle
- 792 Mullins effect
- 794 blowing agent
- 796 naphthenic oil
- 798 blank
- 800 coating
- 802 coated fabric
- 804 coating
- 806 coated cord
- 808 foaming agent
- 810 stress
- 812 compressive stress compression stress
- 814 die swell
- 816 water absorption moisture absorption
- 818 lift (in moulding)
- 820 multiple V-belt
- 822 extender
- 824 extended rubber
- 826 direct injection
- 828 loading chamber loading cell loading space
- 830 spreading machine spreader
- 832 doctor blade doctor knife doctor bar
- 834 coating spreading
- 836 roll-knife coating
- 838 blanket coating
- 840 air knife coating
- 842 friction-roll coating
- 844 floating knife coating
- 846 rolling bank
- 848 roll coating inking
- 850 water absorption hygroscopicity
- 852 Mooney scorch
- 854 compound scorch(ing) premature vulcanization
- 856 short moulding
- 858 bareness
- 860 flameproofing
- 862 neoprene
- 864 air impermeability
- 866 insoluble sulphur polymeric sulphur
- 868 nerve
- 870 non-sulphur vulcanizing system
- 872 non-uniformity polydispersity
- 874 neutral fibre of V-belt neutral axis of V-belt
- 876 non-reinforcing filler inactive filler
- 878 low-molecular substance
- 880 low-pressure moulding
- 882 hose coat
- 884 chamber volume
- 886 apparent density
- 888 volume resistivity
- 890 volumetric feeding
- 892 bulk factor
- 894 upside-down mixing
- 896 filler content filler level
- 898 carbon black content carbon black level
- 900 dry rubber content (DRC)
- 902 carbon black moisture content
- 904 solvent discoloration
- 906 break-down of rubbers
- 908 abrasion
- 910 casting
- 912 resistance
- 914 abrasion resistance wear resistance scuff resistance
- 916 flex life
- 918 ozone resistance
- 920 individual pellet crush resistance
- 922 ageing resistance
- 924 fatigue resistance
- 926 collapse resistance
- 928 scrap
- 930 evaporated rubber latex
- 932 resilience rebound elasticity
- 934 deflashing trimming
- 936 centrifuged rubber latex
- 938 centrifugal casting
- 940 draw-down ratio
- 942 opening force
- 944 vent
- 946 breathing
- 948 warming mill warm-up mill
- 950 warm-up of compound preheating of compound
- 952 flex fatigue
- 954 O-ring seal
- 956 olefin
- 958 bend
- 960 traverse thrust plate
- 962 sheathing head
- 964 sheathing
- 966 braid
- 968 braiding machine
- 970 finishing
- 972 rubberizing
- 974 brightening agent
- 976 optimum vulcanization optimum cure optimum vulcanization degree
- 978 orientation
- 980 drawing
- 982 daylight
- 984 open cell
- 986 cloth mark
- 988 spiral
- 990 ozokerite montan wax
- 992 ozone cracking
- 994 toothed belt indented belt
- 996 armoured hose
- 998 paraffin
- 1000 paraffinic oil
- 1002 paraffins
- 1004 steam channel
- 1006 sheet
- 1008 screw zone
- 1010 upper ram
- 1012 pellet
- 1014 pelletization
- 1016 foam
- 1018 foamed rubber
- 1020 peptizing agent peptizer plasticizing agent
- 1022 strength (of material)
- 1024 adhesion strength
- 1026 carbon black pellet strength
- 1028 tear strength
- 1030 tensile strength
- 1032 pigment
- 1034 field latex
- 1036 plastic, noun
- 1038 plasticity
- 1040 plastic deformation
- 1042 plastic state
- 1044 plasticization
- 1046 rubber plasticizing rubber mastication
- 1048 plastics plasticizing
- 1050 plasticizing unit
- 1052 plasticizing cylinder
- 1054 plasticizing capacity melting capacity
- 1056 plastometer plastimeter rheometer
- 1058 slab
- 1060 direct gate
- 1062 loading tray
- 1064 filler
- 1066 lay flat hose
- 1068 flat belt
- 1070 pneumatic press
- 1072 sole crepe
- 1074 undercut counter draft
- 1076 skim rubber
- 1078 vacuum hose
- 1080 undercure
- 1082 drive
- 1084 binding agent binder bonding agent matrix
- 1086 semi-automatic press
- 1088 semi-hard rubber semiebonite
- 1090 semi-efficient vulcanizing system semi EV system
- 1092 polyaddition
- 1094 polydiene polydiolefin
- 1096 polyisoprene
- 1098 polymer
- 1100 polymerization
- 1102 degree of polymerization
- 1104 polymer compound
- 1106 polymeric plasticizer
- 1108 polysulphide rubber (OT, EOT)
- 1110 polyurethane foam
- 1112 orange peel
- 1114 strain, ε (dimensionless)
- 1116 aspect ratio
- 1118 aspect ratio
- 1120 ash
- 1122 crazing
- 1124 cell
- 1126 poromeric material poromer
- 1128 bale coating
- 1130 liner extruder liner
- 1132 weathering
- 1134 frosting
- 1136 surface treatment
- 1138 surface resistivity
- 1140 surface resistance
- 1142 positive mould
- 1144 working pressure
- 1146 pulverising agent
- 1148 dusting powdering
- 1150 powdered rubber
- 1152 primary material
- 1154 primary accelerator
- 1156 percent elongation
- 1158 profile
- 1160 penetration stain
- 1162 sink mark
- 1164 permeability
- 1166 light transmittance
- 1168 propylene-oxide rubber (GPO)
- 1170 cutting back and forth
- 1172 screening machine
- 1174 ageing protective agent antiageing agent
- 1176 anti-foaming agent
- 1178 strike-through
- 1180 cord V-belt
- 1182 ring gate
- 1184 transparency
- 1186 impact break
- 1188 breakdown voltage disruptive voltage
- 1190 translucency
- 1192 extensometer
- 1194 draw plate calibration
- 1196 mechanical packing
- 1198 silent block
- 1200 elasticity
- 1202 thermoelasticity
- 1204 resin
- 1206 resin rubber
- 1208 rubber-metal article
- 1210 rubber spring
- 1212 pre-coagulate
- 1214 blank
- 1216 pre-vulcanized rubber latex
- 1218 first-order transition
- 1220 transition zone
- 1222 cross mixing
- 1224 mismatch off-register off-set
- 1226 overloading
- 1228 transfer mould
- 1230 transfer pot transfer chamber
- 1232 transfer moulding
- 1234 pressure calibration
- 1236 flash overflow spew ridge
- 1238 flash line
- 1240 flash groove spew groove
- 1242 flash mould
- 1244 tear
- 1246 overcure
- 1248 crosshead T-head
- 1250 crosslink
- 1252 clamping force
- 1254 pressure sensitive adhesive
- 1256 blocking
- 1258 straight head
- 1260 compounding
- 1262 natural rubber
- 1264 natural ageing
- 1266 additive
- 1268 tackifier
- 1270 anti-webbing agent
- 1272 anti-flex-cracking agent
- 1274 blister
- 1276 pyrolytic carbon
- 1278 pyrolysis
- 1280 radiation vulcanization
- 1282 radial crack
- 1284 radical polymerization
- 1286 mould frame mould chase
- 1288 ejector frame
- 1290 impact strength
- 1292 impact resistance
- 1294 blow stress
- 1296 thermoset
- 1298 formulation recipe
- 1300 recycling reprocessing
- 1302 bench marks gauge marks reference marks
- 1304 reclaiming agent
- 1306 digester
- 1308 reclaimed rubber rubber reclaim
- 1310 reclamator
- 1312 recuperation recovery
- 1314 rework
- 1318 relative permittivity dielectric constant (relative)
- 1320 stress relaxation
- 1322 rheology
- 1324 flame retardant fire suppressant
- 1326 vulcanization retarder
- 1328 smoke suppressant
- 1330 furnace black
- 1332 reversion
- 1334 drum press
- 1336 rotational casting
- 1338 graft copolymer
- 1340 graft polymer
- 1342 spider
- 1344 polymer destruction polymer decomposition
- 1346 solvent adhesive
- 1348 light scattering
- 1350 soluble sulphur natural sulphur
- 1352 spreading belt
- 1354 solution polymerization
- 1356 runner
- 1358 branched polymer
- 1360 creamed rubber latex
- 1362 creaming agent
- 1364 creaming
- 1366 hand press
- 1368 knurling of cellular material
- 1370 strain rate
- 1372 water vapour transmission rate
- 1374 shear rate,
- 1376 vulcanization rate cure rate
- 1378 diluent thinner (deprecated)
- 1380 bale cutter
- 1382 cut V-belt
- 1384 V-belt set
- 1386 self-curing
- 1388 self-extinguishing ability
- 1390 self-reinforced elastomer
- 1392 carbon black
- 1394 composite mould family mould
- 1396 sedimentation stability
- 1398 secondary material
- 1400 secondary accelerator booster
- 1402 semi-positive mould
- 1404 release agent
- 1406 antistick
- 1408 serum
- 1410 powder density
- 1412 Schwartz value
- 1414 silicone rubber (MQ, MPVQ, MVQ)
- 1416 network
- 1418 crosslinking agent
- 1420 crosslinking efficiency
- 1422 crosslinking
- 1424 crosslinked polymer
- 1426 glass transition
- 1428 glassy state
- 1430 skim latex
- 1432 shelf life storage life
- 1434 friction
- 1436 wetting agent
- 1438 polymer blend
- 1440 gum compound
- 1442 shrinkage
- 1444 shear head
- 1446 shear stress, ij (Pa)
- 1448 shear flow drag flow
- 1450 ease of ignition
- 1452 hand mould
- 1454 sol
- 1456 coextrusion
- 1458 light transmittance coefficient
- 1460 heat transfer coefficient
- 1462 thermal expansion coefficient
- 1464 storage Young’s modulus
- 1466 storage shear modulus
- 1468 combustion
- 1470 waste incineration
- 1472 coupling agent
- 1474 bonding binding
- 1476 coagulation
- 1478 polymer stabilization
- 1480 stabilizer
- 1482 foam stabilizer
- 1484 standard rubber (SMR, SIR)
- 1486 standard compound
- 1488 ageing
- 1490 shelf ageing
- 1492 oxygen-bomb ageing
- 1494 air-oven ageing
- 1496 static stress
- 1498 random copolymer
- 1500 stereoisomery tacticity
- 1502 stereoisomers
- 1504 stereoregular polymer
- 1506 stereospecific polymerization polyinsertion
- 1508 ejection plate stripper plate
- 1510 mould mark
- 1512 flow marks
- 1514 structure
- 1516 constitutional repeating unit
- 1518 tear resistance
- 1520 pimple
- 1522 molar-mass average molar-weight average
- 1524 relative molecular mass average
- 1526 average degree of polymerization mean degree of polymerization
- 1528 average particle diameter
- 1530 cold polymerization
- 1532 cold vulcanization cold cure
- 1534 knit line weld mark weld line
- 1536 cold flow
- 1538 platen press table
- 1540 draw ratio
- 1542 degree of vulcanization
- 1544 dry rubber
- 1546 sulphide sulphur
- 1548 raw material
- 1550 raw rubber
- 1552 suspension
- 1554 suspension polymerization
- 1556 light stability light resistance
- 1558 pale crepe
- 1560 daylight
- 1562 pig roll roll of rubber compound
- 1564 syndiotactic polymer
- 1566 synergy
- 1568 synthetic rubber
- 1570 pourability
- 1572 bulk density
- 1574 former
- 1576 batch lot
- 1578 angle head
- 1580 film die head sheet die head flat die head
- 1582 screw
- 1584 screw kneading machine screw mixer
- 1586 helix
- 1588 nip
- 1590 tensile stress
- 1592 tensile stress at given elongation
- 1594 tactic polymer
- 1596 tandem extruder
- 1598 hot-melt adhesive
- 1600 elongation at break relative ultimate elongation
- 1602 technical rubber
- 1604 Technically Classified Rubber - TC Rubber
- 1606 flowability
- 1608 cup-flow method
- 1610 spiral test
- 1612 heating/cooling equipment
- 1614 cored screw
- 1616 thermal degradation
- 1618 heat resistance thermal stability
- 1620 thermal conductivity
- 1622 heat stabilizer
- 1624 hot polymerization
- 1626 hot vulcanization heat vulcanization
- 1628 crystallization temperature
- 1630 brittleness temperature
- 1632 pressing temperature
- 1634 self-ignition temperature
- 1636 glass transition temperature
- 1638 melting temperature
- 1640 injection temperature
- 1642 vulcanization temperature
- 1644 thermal expansion
- 1646 temperature coefficient of vulcanization
- 1648 thermal diffusivity
- 1650 thermal black
- 1652 thermoplastic
- 1654 thermoplasticity
- 1656 thermoplastic elastomer (TPE)
- 1658 thermoplastic vulcanizate
- 1660 heat sensitizer
- 1662 terpolymer
- 1664 dough
- 1666 thermoprene
- 1668 thiokol
- 1670 textile reinforcement
- 1672 woven fabric
- 1674 compressive strain
- 1676 pressure hose
- 1678 pressure flow
- 1680 damping
- 1682 cement mastic putty
- 1684 flow line
- 1686 flow path
- 1688 heating plate
- 1690 tensile testing machine
- 1692 crack fissure
- 1694 mandrel
- 1696 tropicalization
- 1698 pipe
- 1700 permanent set
- 1702 elongation set after break
- 1704 compression set
- 1706 tensile set
- 1708 nozzle
- 1710 frictional force
- 1712 friction
- 1714 stiffness
- 1716 spring constant
- 1718 paraffin wax
- 1720 female mould cavity die
- 1722 male mould force
- 1724 shape memory elastic/plastic memory
- 1726 moulding cycle
- 1728 opening surface
- 1730 moulding parts
- 1732 cavity pressure
- 1734 moulding
- 1736 webbing
- 1738 sunlight cracking sunlight checking
- 1740 ebonite hard rubber
- 1742 storage hardening
- 1744 durometer
- 1746 hardness
- 1748 rubber hardness
- 1750 Shore hardness
- 1752 dust stop
- 1754 efficient vulcanizing system EV system
- 1756 V-belt angle
- 1758 angular velocity, ( (rad · s-1)
- 1760 draft draw
- 1762 ultra accelerator
- 1764 artificial weathering
- 1766 fatigue of material
- 1768 tension fatigue
- 1770 bearing capacity load capacity load carrying capacity
- 1772 clamping plate
- 1774 knitted ply knit
- 1776 leaching
- 1778 urethane rubber (AU, EU)
- 1780 vulcanization accelerator
- 1782 delayed-action accelerator
- 1784 sludge
- 1786 decay constant, (s1)
- 1788 bumping
- 1790 closing time
- 1792 clamping unit
- 1794 locking force
- 1796 closed cell
- 1798 mould clamping
- 1800 rubber smoked sheets (RSS)
- 1802 scrap
- 1804 vacuum calibration
- 1806 roller head
- 1808 calender
- 1810 calendering effect
- 1812 calendering
- 1814 roll bowl
- 1816 barrel cylinder
- 1818 calender roll calender bowl
- 1820 extruder barrel
- 1822 variator belt
- 1824 bound sulphur
- 1826 bound rubber
- 1828 bound monomer
- 1830 weighted average particle diameter
- 1832 ejector plate guide
- 1834 fan gate
- 1836 land area mating surface
- 1838 valve
- 1840 weather-o-meter
- 1842 blowing down
- 1844 multicavity mould multi-impression mould
- 1846 multi-screw extruder multiple screw extruder
- 1848 viscoelasticity
- 1850 viscoelastic deformation
- 1852 viscometer viscosimeter
- 1854 Mooney viscometer
- 1856 viscosity
- 1858 Mooney viscosity
- 1862 fibre
- 1864 corrugated hose ringlet hose
- 1866 flocculation
- 1868 hose ply
- 1870 backing plate
- 1872 outer length of V-belt
- 1874 volume resistance
- 1876 dowel bush
- 1878 dowel pin guide pin
- 1880 conductive black
- 1882 water channel
- 1884 free sulphur
- 1886 loose punch
- 1888 wrinkle
- 1890 return spring
- 1892 notched impact strength
- 1894 injection moulding cycle
- 1896 injection mould
- 1898 injection unit
- 1900 injection capacity shot
- 1902 injection plunger injection ram
- 1904 injection force
- 1906 injection moulding machine
- 1908 injection pressure
- 1910 injection nozzle
- 1912 injection cylinder
- 1914 injection moulding
- 1916 injection stamping hybrid moulding
- 1918 feeding zone (of screw)
- 1920 backrinding retracted spew
- 1922 friction ratio
- 1924 frictioning friction coating
- 1926 sprue bush feed bush
- 1928 gate
- 1930 sprue
- 1932 gating system
- 1934 sprue
- 1936 curemeter
- 1938 oscillating-disc curemeter
- 1940 vulcanization cure
- 1942 UHF vulcanization
- 1944 reverting cure peaky cure
- 1946 marching cure
- 1948 plateau cure flat cure
- 1950 vulcanizing agent
- 1952 vulcanizing bladder
- 1954 vulcanizing system curing system
- 1956 sulphurless vulcanizing system
- 1958 vulcanizing plant vulcanizing equipment
- 1960 vulcanized rubber; vulcanizate; rubber
- 1962 curability
- 1964 tinting strength
- 1965 a) see tinting strength
- 1966 air bladder
- 1968 tyre shaper bagging-up machine
- 1970 void
- 1972 ejection ram ejection plunger
- 1974 ejecting device
- 1976 ejector
- 1978 spring ejector
- 1980 sprue ejector
- 1982 ejection
- 1984 bloom
- 1986 chipping chunking
- 1988 moulding
- 1990 duplicate part duplicate plate
- 1992 bleeding
- 1994 estimated length of V-belt
- 1996 estimated width of V-belt
- 1998 estimated pulley diameter
- 2000 roll crown roll camber
- 2002 sheeting
- 2004 production line
- 2006 moulding shrinkage
- 2008 punching pad
- 2010 clicking machine punching machine
- 2012 high-frequency heating
- 2014 high-pressure moulding
- 2016 high-pressure capillary viscometer
- 2018 desiccant
- 2020 injection-moulded piece
- 2022 metering zone homogenizing zone
- 2024 sliding punch
- 2026 extractor
- 2028 extrusion head
- 2030 extrusion coating
- 2032 extruder
- 2034 vented extruder
- 2036 mass flow rate
- 2038 extrusion
- 2040 plucking
- 2042 thermosetting, adjective
- 2044 curing agent
- 2046 reinforcement
- 2048 hose reinforcing ply
- 2050 compatibility
- 2052 air separator
- 2054 wicking
- 2056 ignition
- 2058 colour staining
- 2060 sample
- 2062 hose wrapping
- 2064 traction bar
- 2066 seizing of mould
- 2068 heat build-up
- 2070 concentrated rubber latex
- 2072 thickener
- 2074 haze
- 2076 twist
- 2078 insert
- 2080 fogging
- 2082 entanglement
- 2084 landfilling
- 2086 screw pin screw core
- 2088 screw ring
- 2090 collapse
- 2092 warp warping
- 2094 apparent viscosity
- 2096 medical rubber goods
- 2098 doubling
- 2100 quencher
- 2102 zinc white
- 2104 refining mill
- 2106 abrasion test
- 2108 test piece specimen
- 2110 ring
- 2112 dumb-bell
- 2114 plasticizer softener
- 2116 zone
- 2118 recovery
- 2120 return pin
- 2122 back pressure
- 2124 back pressure flow
- 2126 processability processibility
- 2128 delta Mooney processability
- 2130 processing aid
- 2132 process(ing) oil
- 2134 grain
- 2136 accelerated ageing
- 2138 abrasion loss
- 2140 loss constant
- 2146 loss Young’s modulus
- 2148 loss shear modulus
- 2150 loss angle, (rad)
- 2152 heating loss
- 2154 stiffener
- 2156 reinforcing filler
- 2158 reinforcing agent
- 2160 restricted gate
- 2162 gelation
- 2164 gelling agent
- 2166 durability useful life
- 2168 service life of a mould
- 2170 yellow crepe
‹
Nahlásit chybu
273 root-mean-square stress
root-mean-square stress
square root of the mean value of the square of the stress averaged over one cycle of deformation
NOTE For a symmetrical sinusoidal stress, the root-mean-square stress equals the stress amplitude divided by
.273 efektivní hodnota napětí
efektivní hodnota napětí
druhá odmocnina střední hodnoty kvadrátu napětí pro jeden deformační cyklus
POZNÁMKA Pro symetrické sinusové napětí se střední kvadratické napětí rovná amplitudě napětí dělené
.