- 1 UV absorber light stabilizer
- 3 dibutyl phthalate absorption number
- 5 oil absorption number (OAN)
- 7 adhesion
- 9 adiabatic extrusion autothermal extrusion
- 11 addition polymerization
- 13 agglomeration
- 15 agglomerate
- 18 aggregate
- 20 acrylic rubber (ACM, AEM)
- 22 activator
- 24 kicker
- 26 vulcanization activator
- 28 active zinc oxide
- 30 alkane
- 32 alkene olefin
- 34 alternating copolymer
- 36 strain amplitude
- 38 anaerobic adhesive
- 40 anionic polymerization
- 42 antiblocking agent
- 44 antidegradant
- 46 staining antidegradant
- 48 non-staining antidegradant
- 50 anticoagulant
- 52 antioxidant
- 54 antiozonant
- 56 antistatic agent
- 58 applied skin
- 60 size finish
- 62 aromatic oil
- 64 atactic polymer
- 66 attritor
- 68 autoclave
- 70 automatic ejection
- 72 autoheating screw self-heating screw
- 74 balata
- 76 wrapping
- 78 light fastness colour fastness (on exposure to light)
- 80 colour
- 82 colorant
- 84 dyestuff
- 86 tinting strength
- 88 whiteness
- 90 ram
- 92 rotorless curemeter
- 94 solventless adhesive solvent-free adhesive
- 96 screwless extruder
- 98 white spots wet spots virgin rubber (depreciated)
- 100 biological resistance
- 102 biological stabilizer
- 104 block
- 106 bulk polymerization mass polymerization
- 108 block copolymer
- 110 swelling
- 112 tip (of rotor)
- 114 bubble
- 116 acrylonitrile-butadiene rubber (NBR) nitrile rubber
- 118 butadiene rubber (BR)
- 120 styrene-butadiene rubber (SBR)
- 122 butyl rubber (IIR)
- 124 total sulphur
- 126 total solids (TS) residue after drying
- 128 spider line
- 130 pot life working life
- 132 particle
- 134 KOH number
- 136 plasticity number
- 138 volatile fatty acid number
- 140 strainer
- 142 straining
- 144 dose
- 146 deflocculating agent deflocculant
- 148 strain deformation
- 150 mould swelling
- 152 polymer degradation
- 154 bar mould
- 156 split screw parted screw
- 158 parting plane
- 160 chain length
- 162 deodorant deodorizer
- 164 depolymerization
- 166 derivative
- 168 embossing
- 170 platen
- 172 polymer destruction
- 174 devulcanization
- 176 hydroperoxide scavenger hydroperoxide deactivator
- 178 dielectric strength
- 180 dielectric heating
- 182 diene diolefin
- 184 diene rubber
- 186 hole pinhole
- 188 dispersion
- 190 dispersing agent
- 192 dispersion
- 194 dispersion adhesive
- 196 dispersion polymerization
- 198 molar weight distribution
- 200 pellet size distribution
- 202 molar (molecular) mass distribution curve molar (molecular) weight distribution curve
- 204 closed assembly time
- 206 moulding cycle time
- 208 moulding time
- 210 scorch time
- 212 open assembly time
- 214 mould filling time
- 216 dwell time residence time
- 218 dry tack time
- 220 afterbake stoving postheating
- 222 aftercure postcure
- 224 bottom ejection
- 226 upstroke press
- 228 sulphur donor
- 230 conveyor conveyer
- 232 granulate conveyor granulate feeder
- 234 pressure pad
- 236 flash land
- 238 holding pressure
- 240 smouldering
- 242 aftercure postcure
- 244 maturation
- 246 crushing breaking
- 248 roughness
- 250 crusher
- 252 phr
- 254 hose lining
- 256 mould cavity
- 258 hollow article
- 260 twin-screw extruder
- 262 two-roll mill roll mill open mill
- 267 dynamic vulcanization
- 269 dynamic stress
- 271 root-mean-square strain
- 273 root-mean-square stress
- 275 elasticity
- 277 elastic deformation
- 279 elastomer
- 281 electric breakdown electric disruption
- 283 electrodecantation
- 285 electromagnetic separator
- 287 emulsification
- 289 emulsifier
- 291 emulsion
- 293 emulsion polymerization
- 295 epichlorhydrin rubber (CO, ECO)
- 297 ester-urethane rubber (AU)
- 299 floating plate
- 301 multiplaten press multidaylight press
- 303 ether-urethane rubber (EU)
- 305 ethylene-propylene rubber (EPM, EPDM)
- 307 extractable sulphur
- 309 extraction stain
- 311 extrudate
- 313 factice
- 315 phase state
- 317 film
- 319 flexometer
- 321 flocculating agent flocculant
- 323 fluorocarbon rubber (FPM, FKM, FFKM, CFM)
- 325 film
- 327 mould
- 329 photooxidation
- 331 mineral rubber
- 333 physical expanding
- 335 physical modification
- 337 gel
- 339 (rubber) gel
- 341 Gough-Joule effect
- 343 granulate granular compound
- 345 granulation
- 347 granulated rubber beaded rubber
- 349 guayule rubber
- 351 rubber compound
- 353 rubber-metal
- 355 rubber-metal spring
- 357 friction calender
- 359 gutta-percha
- 361 hose
- 363 hose assembly
- 365 woven hose
- 367 braided hose
- 369 spiralled hose
- 371 knitted hose
- 373 wrapped ply hose
- 375 hard wall hose
- 377 Hevea brasiliensis
- 379 gravimetric feeding
- 381 rotor
- 383 kneading
- 385 internal mixer kneader
- 390 homogenization
- 392 compatibilizer
- 394 homopolymer
- 396 top ejection
- 398 downstroke press
- 400 burn, noun
- 402 flammability combustibility
- 404 sponge rubber
- 406 die
- 408 network chain density
- 412 hydraulic press
- 414 rubber hydrochloride
- 416 hydrolysis
- 418 hydromechanical press
- 420 hysteresis
- 422 hysteresis loop
- 424 hysteresis loss
- 426 chemical modification
- 428 chemical resistance
- 430 chemical foaming
- 432 cooling jig cooling fixture shrinkage block shrinkage jig
- 434 refrigerator
- 436 chlorinated rubber
- 438 chloroprene rubber (CR)
- 440 chlorsulfonated polyethylene (CSM)
- 442 ideal elastic deformation
- 444 die line
- 446 impregnation proofing
- 448 impregnating agent
- 450 impregnating machine impregnator
- 452 index of non-uniformity index of polydispersity degree of polydispersity
- 454 abrasion resistance index
- 456 plasticity retention index
- 458 induction heating
- 460 inert filler
- 462 inhibitor
- 464 scorch inhibitor pre-vulcanization inhibitor
- 466 intrusion flow moulding
- 468 inverse coating
- 470 ionic polymerization
- 472 isoprene rubber (IR) synthetic polyisoprene
- 474 insulation resistance
- 476 isomer
- 478 isotactic polymer
- 480 single-cavity mould
- 482 single-screw extruder
- 484 fine particles
- 486 iodine adsorption number
- 488 rosin colophony
- 490 calibration gauging sizing
- 492 channel black
- 494 liquid curing medium salt bath
- 496 liquid rubber
- 498 capillary viscometer
- 500 carboxylated rubber
- 502 rotary moulding
- 504 cationic polymerization
- 506 rubber
- 508 oil-extended rubber
- 510 rubber-like state viscoelastic state
- 512 rubber tree
- 514 rubber poison
- 516 rubber latex
- 518 rubber sol
- 520 rubber hydrocarbon
- 522 viscosity/density ratio
- 524 V-belt
- 526 talcing
- 528 wicking
- 530 coagulant dipping
- 532 coagulant
- 534 coagulate
- 536 pin core
- 538 insert pin
- 540 pin barrel extruder
- 542 colloid mill
- 544 (mixer) chamber
- 546 assembling
- 548 complex Young’s modulus
- 550 complex shear modulus
- 552 composting
- 554 composite material composite
- 558 compression ratio
- 560 crosslink concentration crosslink density
- 562 concentration coefficient of vulcanization
- 564 masterbatch mother stock
- 566 natural latex concentrate
- 568 tube ending
- 570 conditioning
- 572 environmental conditioning
- 574 building
- 576 tyre-building drum
- 578 tack
- 580 building machine
- 582 tyre building machine
- 584 configuration
- 586 conformation
- 588 contact adhesive
- 590 contact stain
- 592 continuous vulcanization
- 594 conventional vulcanizing system
- 596 preservative
- 598 preserved rubber latex stabilized rubber latex
- 600 copolymer
- 602 copolymerization
- 604 cord (fabric)
- 606 cord fabric V-belt
- 608 corrosion
- 610 stress cracking
- 612 anchor plate
- 614 crater pit hole
- 616 beading (the end)
- 618 necking
- 620 creep
- 622 creep modulus
- 624 crystalline state
- 626 chalking
- 628 ball mill
- 630 skin
- 632 breaker plate
- 634 latex
- 636 latex foam
- 638 latex compound
- 640 cellular material
- 642 core cellular material
- 644 sponge material open cell foam
- 646 foamed material
- 648 expanded rubber
- 650 cellular hard rubber cellular ebonite
- 652 expanded adhesive
- 654 expanding
- 656 structural foam
- 658 bonding
- 660 solvent bonding
- 662 adhesive
- 664 gloss
- 666 mechanical fatigue limit
- 668 limiting oxygen index
- 670 limiting threshold strain
- 672 linear polymer
- 674 press
- 676 moulding cycle
- 678 compression mould
- 680 moulding force
- 682 moulding pressure
- 684 compression moulding
- 686 direct compacting
- 688 impact moulding
- 690 bag moulding
- 692 casting
- 694 logarithmic decrement
- 696 fatigue breakdown
- 698 dipping
- 700 dipped article
- 702 macromolecule
- 704 macromolecular substance
- 706 macroradical
- 708 lubricant
- 710 mould-release agent mould lubricant
- 712 mechanical stability
- 714 mechanical conditioning
- 716 mechanical gasket
- 718 mechano-chemical modification
- 720 mechanical press
- 722 mechanical loss factor, tg (
- 724 mechanical loss angle
- 726 cellular rubber
- 728 soft rubber
- 730 specific gravity
- 732 specific heat capacity
- 734 measured length gauge length
- 736 dynamic fatigue life
- 738 yield point tensile strength at yield
- 740 flexural strength flex resistance
- 742 shear strength
- 743 maximum stress developed in the test piece, defined as τ = F / S, where F is the force acting on cross section S; under prescribed conditions the test piece breaks at this stress
- 744 International Rubber Hardness Degrees (IRHD)
- 746 leakage flow
- 748 migration
- 750 migration stain
- 752 mixer agitator
- 754 mixing
- 756 microporous rubber
- 758 microhardness
- 760 (oil treated) rubber-maker sulphur
- 762 grinding
- 764 ground vulcanized rubber
- 766 grinding mill
- 768 modification
- 770 rubber chain modification at vulcanization
- 772 polymer modification
- 774 modifier
- 776 modulus of elasticity complex modulus of elasticity
- 778 Young’s modulus
- 780 shear modulus
- 782 molar weight molar mass
- 784 molecular mass molecular weight
- 786 monomer
- 788 monomeric unit mer
- 790 mottle
- 792 Mullins effect
- 794 blowing agent
- 796 naphthenic oil
- 798 blank
- 800 coating
- 802 coated fabric
- 804 coating
- 806 coated cord
- 808 foaming agent
- 810 stress
- 812 compressive stress compression stress
- 814 die swell
- 816 water absorption moisture absorption
- 818 lift (in moulding)
- 820 multiple V-belt
- 822 extender
- 824 extended rubber
- 826 direct injection
- 828 loading chamber loading cell loading space
- 830 spreading machine spreader
- 832 doctor blade doctor knife doctor bar
- 834 coating spreading
- 836 roll-knife coating
- 838 blanket coating
- 840 air knife coating
- 842 friction-roll coating
- 844 floating knife coating
- 846 rolling bank
- 848 roll coating inking
- 850 water absorption hygroscopicity
- 852 Mooney scorch
- 854 compound scorch(ing) premature vulcanization
- 856 short moulding
- 858 bareness
- 860 flameproofing
- 862 neoprene
- 864 air impermeability
- 866 insoluble sulphur polymeric sulphur
- 868 nerve
- 870 non-sulphur vulcanizing system
- 872 non-uniformity polydispersity
- 874 neutral fibre of V-belt neutral axis of V-belt
- 876 non-reinforcing filler inactive filler
- 878 low-molecular substance
- 880 low-pressure moulding
- 882 hose coat
- 884 chamber volume
- 886 apparent density
- 888 volume resistivity
- 890 volumetric feeding
- 892 bulk factor
- 894 upside-down mixing
- 896 filler content filler level
- 898 carbon black content carbon black level
- 900 dry rubber content (DRC)
- 902 carbon black moisture content
- 904 solvent discoloration
- 906 break-down of rubbers
- 908 abrasion
- 910 casting
- 912 resistance
- 914 abrasion resistance wear resistance scuff resistance
- 916 flex life
- 918 ozone resistance
- 920 individual pellet crush resistance
- 922 ageing resistance
- 924 fatigue resistance
- 926 collapse resistance
- 928 scrap
- 930 evaporated rubber latex
- 932 resilience rebound elasticity
- 934 deflashing trimming
- 936 centrifuged rubber latex
- 938 centrifugal casting
- 940 draw-down ratio
- 942 opening force
- 944 vent
- 946 breathing
- 948 warming mill warm-up mill
- 950 warm-up of compound preheating of compound
- 952 flex fatigue
- 954 O-ring seal
- 956 olefin
- 958 bend
- 960 traverse thrust plate
- 962 sheathing head
- 964 sheathing
- 966 braid
- 968 braiding machine
- 970 finishing
- 972 rubberizing
- 974 brightening agent
- 976 optimum vulcanization optimum cure optimum vulcanization degree
- 978 orientation
- 980 drawing
- 982 daylight
- 984 open cell
- 986 cloth mark
- 988 spiral
- 990 ozokerite montan wax
- 992 ozone cracking
- 994 toothed belt indented belt
- 996 armoured hose
- 998 paraffin
- 1000 paraffinic oil
- 1002 paraffins
- 1004 steam channel
- 1006 sheet
- 1008 screw zone
- 1010 upper ram
- 1012 pellet
- 1014 pelletization
- 1016 foam
- 1018 foamed rubber
- 1020 peptizing agent peptizer plasticizing agent
- 1022 strength (of material)
- 1024 adhesion strength
- 1026 carbon black pellet strength
- 1028 tear strength
- 1030 tensile strength
- 1032 pigment
- 1034 field latex
- 1036 plastic, noun
- 1038 plasticity
- 1040 plastic deformation
- 1042 plastic state
- 1044 plasticization
- 1046 rubber plasticizing rubber mastication
- 1048 plastics plasticizing
- 1050 plasticizing unit
- 1052 plasticizing cylinder
- 1054 plasticizing capacity melting capacity
- 1056 plastometer plastimeter rheometer
- 1058 slab
- 1060 direct gate
- 1062 loading tray
- 1064 filler
- 1066 lay flat hose
- 1068 flat belt
- 1070 pneumatic press
- 1072 sole crepe
- 1074 undercut counter draft
- 1076 skim rubber
- 1078 vacuum hose
- 1080 undercure
- 1082 drive
- 1084 binding agent binder bonding agent matrix
- 1086 semi-automatic press
- 1088 semi-hard rubber semiebonite
- 1090 semi-efficient vulcanizing system semi EV system
- 1092 polyaddition
- 1094 polydiene polydiolefin
- 1096 polyisoprene
- 1098 polymer
- 1100 polymerization
- 1102 degree of polymerization
- 1104 polymer compound
- 1106 polymeric plasticizer
- 1108 polysulphide rubber (OT, EOT)
- 1110 polyurethane foam
- 1112 orange peel
- 1114 strain, ε (dimensionless)
- 1116 aspect ratio
- 1118 aspect ratio
- 1120 ash
- 1122 crazing
- 1124 cell
- 1126 poromeric material poromer
- 1128 bale coating
- 1130 liner extruder liner
- 1132 weathering
- 1134 frosting
- 1136 surface treatment
- 1138 surface resistivity
- 1140 surface resistance
- 1142 positive mould
- 1144 working pressure
- 1146 pulverising agent
- 1148 dusting powdering
- 1150 powdered rubber
- 1152 primary material
- 1154 primary accelerator
- 1156 percent elongation
- 1158 profile
- 1160 penetration stain
- 1162 sink mark
- 1164 permeability
- 1166 light transmittance
- 1168 propylene-oxide rubber (GPO)
- 1170 cutting back and forth
- 1172 screening machine
- 1174 ageing protective agent antiageing agent
- 1176 anti-foaming agent
- 1178 strike-through
- 1180 cord V-belt
- 1182 ring gate
- 1184 transparency
- 1186 impact break
- 1188 breakdown voltage disruptive voltage
- 1190 translucency
- 1192 extensometer
- 1194 draw plate calibration
- 1196 mechanical packing
- 1198 silent block
- 1200 elasticity
- 1202 thermoelasticity
- 1204 resin
- 1206 resin rubber
- 1208 rubber-metal article
- 1210 rubber spring
- 1212 pre-coagulate
- 1214 blank
- 1216 pre-vulcanized rubber latex
- 1218 first-order transition
- 1220 transition zone
- 1222 cross mixing
- 1224 mismatch off-register off-set
- 1226 overloading
- 1228 transfer mould
- 1230 transfer pot transfer chamber
- 1232 transfer moulding
- 1234 pressure calibration
- 1236 flash overflow spew ridge
- 1238 flash line
- 1240 flash groove spew groove
- 1242 flash mould
- 1244 tear
- 1246 overcure
- 1248 crosshead T-head
- 1250 crosslink
- 1252 clamping force
- 1254 pressure sensitive adhesive
- 1256 blocking
- 1258 straight head
- 1260 compounding
- 1262 natural rubber
- 1264 natural ageing
- 1266 additive
- 1268 tackifier
- 1270 anti-webbing agent
- 1272 anti-flex-cracking agent
- 1274 blister
- 1276 pyrolytic carbon
- 1278 pyrolysis
- 1280 radiation vulcanization
- 1282 radial crack
- 1284 radical polymerization
- 1286 mould frame mould chase
- 1288 ejector frame
- 1290 impact strength
- 1292 impact resistance
- 1294 blow stress
- 1296 thermoset
- 1298 formulation recipe
- 1300 recycling reprocessing
- 1302 bench marks gauge marks reference marks
- 1304 reclaiming agent
- 1306 digester
- 1308 reclaimed rubber rubber reclaim
- 1310 reclamator
- 1312 recuperation recovery
- 1314 rework
- 1318 relative permittivity dielectric constant (relative)
- 1320 stress relaxation
- 1322 rheology
- 1324 flame retardant fire suppressant
- 1326 vulcanization retarder
- 1328 smoke suppressant
- 1330 furnace black
- 1332 reversion
- 1334 drum press
- 1336 rotational casting
- 1338 graft copolymer
- 1340 graft polymer
- 1342 spider
- 1344 polymer destruction polymer decomposition
- 1346 solvent adhesive
- 1348 light scattering
- 1350 soluble sulphur natural sulphur
- 1352 spreading belt
- 1354 solution polymerization
- 1356 runner
- 1358 branched polymer
- 1360 creamed rubber latex
- 1362 creaming agent
- 1364 creaming
- 1366 hand press
- 1368 knurling of cellular material
- 1370 strain rate
- 1372 water vapour transmission rate
- 1374 shear rate,
- 1376 vulcanization rate cure rate
- 1378 diluent thinner (deprecated)
- 1380 bale cutter
- 1382 cut V-belt
- 1384 V-belt set
- 1386 self-curing
- 1388 self-extinguishing ability
- 1390 self-reinforced elastomer
- 1392 carbon black
- 1394 composite mould family mould
- 1396 sedimentation stability
- 1398 secondary material
- 1400 secondary accelerator booster
- 1402 semi-positive mould
- 1404 release agent
- 1406 antistick
- 1408 serum
- 1410 powder density
- 1412 Schwartz value
- 1414 silicone rubber (MQ, MPVQ, MVQ)
- 1416 network
- 1418 crosslinking agent
- 1420 crosslinking efficiency
- 1422 crosslinking
- 1424 crosslinked polymer
- 1426 glass transition
- 1428 glassy state
- 1430 skim latex
- 1432 shelf life storage life
- 1434 friction
- 1436 wetting agent
- 1438 polymer blend
- 1440 gum compound
- 1442 shrinkage
- 1444 shear head
- 1446 shear stress, ij (Pa)
- 1448 shear flow drag flow
- 1450 ease of ignition
- 1452 hand mould
- 1454 sol
- 1456 coextrusion
- 1458 light transmittance coefficient
- 1460 heat transfer coefficient
- 1462 thermal expansion coefficient
- 1464 storage Young’s modulus
- 1466 storage shear modulus
- 1468 combustion
- 1470 waste incineration
- 1472 coupling agent
- 1474 bonding binding
- 1476 coagulation
- 1478 polymer stabilization
- 1480 stabilizer
- 1482 foam stabilizer
- 1484 standard rubber (SMR, SIR)
- 1486 standard compound
- 1488 ageing
- 1490 shelf ageing
- 1492 oxygen-bomb ageing
- 1494 air-oven ageing
- 1496 static stress
- 1498 random copolymer
- 1500 stereoisomery tacticity
- 1502 stereoisomers
- 1504 stereoregular polymer
- 1506 stereospecific polymerization polyinsertion
- 1508 ejection plate stripper plate
- 1510 mould mark
- 1512 flow marks
- 1514 structure
- 1516 constitutional repeating unit
- 1518 tear resistance
- 1520 pimple
- 1522 molar-mass average molar-weight average
- 1524 relative molecular mass average
- 1526 average degree of polymerization mean degree of polymerization
- 1528 average particle diameter
- 1530 cold polymerization
- 1532 cold vulcanization cold cure
- 1534 knit line weld mark weld line
- 1536 cold flow
- 1538 platen press table
- 1540 draw ratio
- 1542 degree of vulcanization
- 1544 dry rubber
- 1546 sulphide sulphur
- 1548 raw material
- 1550 raw rubber
- 1552 suspension
- 1554 suspension polymerization
- 1556 light stability light resistance
- 1558 pale crepe
- 1560 daylight
- 1562 pig roll roll of rubber compound
- 1564 syndiotactic polymer
- 1566 synergy
- 1568 synthetic rubber
- 1570 pourability
- 1572 bulk density
- 1574 former
- 1576 batch lot
- 1578 angle head
- 1580 film die head sheet die head flat die head
- 1582 screw
- 1584 screw kneading machine screw mixer
- 1586 helix
- 1588 nip
- 1590 tensile stress
- 1592 tensile stress at given elongation
- 1594 tactic polymer
- 1596 tandem extruder
- 1598 hot-melt adhesive
- 1600 elongation at break relative ultimate elongation
- 1602 technical rubber
- 1604 Technically Classified Rubber - TC Rubber
- 1606 flowability
- 1608 cup-flow method
- 1610 spiral test
- 1612 heating/cooling equipment
- 1614 cored screw
- 1616 thermal degradation
- 1618 heat resistance thermal stability
- 1620 thermal conductivity
- 1622 heat stabilizer
- 1624 hot polymerization
- 1626 hot vulcanization heat vulcanization
- 1628 crystallization temperature
- 1630 brittleness temperature
- 1632 pressing temperature
- 1634 self-ignition temperature
- 1636 glass transition temperature
- 1638 melting temperature
- 1640 injection temperature
- 1642 vulcanization temperature
- 1644 thermal expansion
- 1646 temperature coefficient of vulcanization
- 1648 thermal diffusivity
- 1650 thermal black
- 1652 thermoplastic
- 1654 thermoplasticity
- 1656 thermoplastic elastomer (TPE)
- 1658 thermoplastic vulcanizate
- 1660 heat sensitizer
- 1662 terpolymer
- 1664 dough
- 1666 thermoprene
- 1668 thiokol
- 1670 textile reinforcement
- 1672 woven fabric
- 1674 compressive strain
- 1676 pressure hose
- 1678 pressure flow
- 1680 damping
- 1682 cement mastic putty
- 1684 flow line
- 1686 flow path
- 1688 heating plate
- 1690 tensile testing machine
- 1692 crack fissure
- 1694 mandrel
- 1696 tropicalization
- 1698 pipe
- 1700 permanent set
- 1702 elongation set after break
- 1704 compression set
- 1706 tensile set
- 1708 nozzle
- 1710 frictional force
- 1712 friction
- 1714 stiffness
- 1716 spring constant
- 1718 paraffin wax
- 1720 female mould cavity die
- 1722 male mould force
- 1724 shape memory elastic/plastic memory
- 1726 moulding cycle
- 1728 opening surface
- 1730 moulding parts
- 1732 cavity pressure
- 1734 moulding
- 1736 webbing
- 1738 sunlight cracking sunlight checking
- 1740 ebonite hard rubber
- 1742 storage hardening
- 1744 durometer
- 1746 hardness
- 1748 rubber hardness
- 1750 Shore hardness
- 1752 dust stop
- 1754 efficient vulcanizing system EV system
- 1756 V-belt angle
- 1758 angular velocity, ( (rad · s-1)
- 1760 draft draw
- 1762 ultra accelerator
- 1764 artificial weathering
- 1766 fatigue of material
- 1768 tension fatigue
- 1770 bearing capacity load capacity load carrying capacity
- 1772 clamping plate
- 1774 knitted ply knit
- 1776 leaching
- 1778 urethane rubber (AU, EU)
- 1780 vulcanization accelerator
- 1782 delayed-action accelerator
- 1784 sludge
- 1786 decay constant, (s1)
- 1788 bumping
- 1790 closing time
- 1792 clamping unit
- 1794 locking force
- 1796 closed cell
- 1798 mould clamping
- 1800 rubber smoked sheets (RSS)
- 1802 scrap
- 1804 vacuum calibration
- 1806 roller head
- 1808 calender
- 1810 calendering effect
- 1812 calendering
- 1814 roll bowl
- 1816 barrel cylinder
- 1818 calender roll calender bowl
- 1820 extruder barrel
- 1822 variator belt
- 1824 bound sulphur
- 1826 bound rubber
- 1828 bound monomer
- 1830 weighted average particle diameter
- 1832 ejector plate guide
- 1834 fan gate
- 1836 land area mating surface
- 1838 valve
- 1840 weather-o-meter
- 1842 blowing down
- 1844 multicavity mould multi-impression mould
- 1846 multi-screw extruder multiple screw extruder
- 1848 viscoelasticity
- 1850 viscoelastic deformation
- 1852 viscometer viscosimeter
- 1854 Mooney viscometer
- 1856 viscosity
- 1858 Mooney viscosity
- 1862 fibre
- 1864 corrugated hose ringlet hose
- 1866 flocculation
- 1868 hose ply
- 1870 backing plate
- 1872 outer length of V-belt
- 1874 volume resistance
- 1876 dowel bush
- 1878 dowel pin guide pin
- 1880 conductive black
- 1882 water channel
- 1884 free sulphur
- 1886 loose punch
- 1888 wrinkle
- 1890 return spring
- 1892 notched impact strength
- 1894 injection moulding cycle
- 1896 injection mould
- 1898 injection unit
- 1900 injection capacity shot
- 1902 injection plunger injection ram
- 1904 injection force
- 1906 injection moulding machine
- 1908 injection pressure
- 1910 injection nozzle
- 1912 injection cylinder
- 1914 injection moulding
- 1916 injection stamping hybrid moulding
- 1918 feeding zone (of screw)
- 1920 backrinding retracted spew
- 1922 friction ratio
- 1924 frictioning friction coating
- 1926 sprue bush feed bush
- 1928 gate
- 1930 sprue
- 1932 gating system
- 1934 sprue
- 1936 curemeter
- 1938 oscillating-disc curemeter
- 1940 vulcanization cure
- 1942 UHF vulcanization
- 1944 reverting cure peaky cure
- 1946 marching cure
- 1948 plateau cure flat cure
- 1950 vulcanizing agent
- 1952 vulcanizing bladder
- 1954 vulcanizing system curing system
- 1956 sulphurless vulcanizing system
- 1958 vulcanizing plant vulcanizing equipment
- 1960 vulcanized rubber; vulcanizate; rubber
- 1962 curability
- 1964 tinting strength
- 1965 a) see tinting strength
- 1966 air bladder
- 1968 tyre shaper bagging-up machine
- 1970 void
- 1972 ejection ram ejection plunger
- 1974 ejecting device
- 1976 ejector
- 1978 spring ejector
- 1980 sprue ejector
- 1982 ejection
- 1984 bloom
- 1986 chipping chunking
- 1988 moulding
- 1990 duplicate part duplicate plate
- 1992 bleeding
- 1994 estimated length of V-belt
- 1996 estimated width of V-belt
- 1998 estimated pulley diameter
- 2000 roll crown roll camber
- 2002 sheeting
- 2004 production line
- 2006 moulding shrinkage
- 2008 punching pad
- 2010 clicking machine punching machine
- 2012 high-frequency heating
- 2014 high-pressure moulding
- 2016 high-pressure capillary viscometer
- 2018 desiccant
- 2020 injection-moulded piece
- 2022 metering zone homogenizing zone
- 2024 sliding punch
- 2026 extractor
- 2028 extrusion head
- 2030 extrusion coating
- 2032 extruder
- 2034 vented extruder
- 2036 mass flow rate
- 2038 extrusion
- 2040 plucking
- 2042 thermosetting, adjective
- 2044 curing agent
- 2046 reinforcement
- 2048 hose reinforcing ply
- 2050 compatibility
- 2052 air separator
- 2054 wicking
- 2056 ignition
- 2058 colour staining
- 2060 sample
- 2062 hose wrapping
- 2064 traction bar
- 2066 seizing of mould
- 2068 heat build-up
- 2070 concentrated rubber latex
- 2072 thickener
- 2074 haze
- 2076 twist
- 2078 insert
- 2080 fogging
- 2082 entanglement
- 2084 landfilling
- 2086 screw pin screw core
- 2088 screw ring
- 2090 collapse
- 2092 warp warping
- 2094 apparent viscosity
- 2096 medical rubber goods
- 2098 doubling
- 2100 quencher
- 2102 zinc white
- 2104 refining mill
- 2106 abrasion test
- 2108 test piece specimen
- 2110 ring
- 2112 dumb-bell
- 2114 plasticizer softener
- 2116 zone
- 2118 recovery
- 2120 return pin
- 2122 back pressure
- 2124 back pressure flow
- 2126 processability processibility
- 2128 delta Mooney processability
- 2130 processing aid
- 2132 process(ing) oil
- 2134 grain
- 2136 accelerated ageing
- 2138 abrasion loss
- 2140 loss constant
- 2146 loss Young’s modulus
- 2148 loss shear modulus
- 2150 loss angle, (rad)
- 2152 heating loss
- 2154 stiffener
- 2156 reinforcing filler
- 2158 reinforcing agent
- 2160 restricted gate
- 2162 gelation
- 2164 gelling agent
- 2166 durability useful life
- 2168 service life of a mould
- 2170 yellow crepe
‹
Nahlásit chybu
2118 recovery
recovery
time-dependent decrease in strain following removal of stress
NOTE Instantaneous recovery is excluded.
2118 zotavení
zotavení
časově závislý pokles deformace po uvolnění napětí
POZNÁMKA Okamžité zotavení je vyloučeno.